ABS片材挤出成型, 型材挤出成型, 热成型

Jamplast JPLGABSE

丙烯腈丁二烯苯乙烯

 

Jamplast, Inc.

 

Technical Data

 

产品说明

 

Jamplast ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.

 

The sheet and thermoforming grades of Jamplast ABS resins provide excellent high and low gloss aesthetics, thermal color stability, heat and impact resistance and stiffness for applications such as luggage, tool cases, burial vault liners, signs and recreation vehicles. Jamplast ABS resins can fill a variety of needs by offering ranges in melt flow rates from 1.0 to 4.0 g/10 min., sheet Izod impacts from 2.5 to 10.5 ft-lb/in and sheet flexural modulus from 285,000 to 300,000 psi.

 

This resin is the lowest gloss and highest melt flow rate option of our ABS sheet grades. With a melt flow rate of 4.0 g/10 min., JPLGABSE can be used for low gloss, low impact applications where easy processability is desired.

 

总体

 

材料状态 • 已商用：当前有效

供货地区 • 北美洲

形式 • 粒子

加工方法 • 片材挤出成型 • 型材挤出成型

• 热成型 • 注射成型

物理性能 额定值单位制 测试方法

比重 1.04g/cm³ ASTM D792

熔流率（熔体流动速率） (230°C/3.8 kg) 3.9g/10 min ASTM D1238

收缩率 - 流动 0.40 到 0.70% ASTM D955

机械性能 额定值单位制 测试方法

拉伸模量 2 1860MPa ASTM D638

抗张强度 2 ASTM D638

屈服 30.3MPa

断裂 31.7MPa

伸长率 2 (断裂) 50% ASTM D638

弯曲模量 3 2210MPa ASTM D790

弯曲强度 3 62.1MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 ASTM D256

-18°C, 3.18 mm 4 80J/m

23°C, 3.18 mm 5 130J/m

落锤冲击 ASTM D3029

-18°C, 2.54 mm 19.8J

23°C, 2.54 mm 22.6J

硬度 额定值单位制 测试方法

洛氏硬度 ASTM D785

L 计秤 80

R 级 108

热性能 额定值单位制 测试方法

载荷下热变形温度 (1.8 MPa, 未退火, 3.18 mm) 96.1°C ASTM D648

维卡软化温度 104°C ASTM D1525

可燃性 额定值单位制 测试方法

UL 阻燃等级 (1.52 mm) HB UL 94

 

Jamplast JPLGABSE

丙烯腈丁二烯苯乙烯

Jamplast, Inc.

注射 额定值单位制

干燥温度 82.2 到 87.8°C

干燥时间 2.0 到 4.0hr

建议的最大水分含量 0.10%

加工（熔体）温度 218 到 274°C

模具温度 26.7 到 60.0°C

背压 0.345 到 3.45MPa

锁模力 2.8 到 6.9kN/cm²

螺杆长径比 20.0:1.0

螺杆压缩比 1.5:1.0 至 3.5:1.0

 

 

 

 